| Chemistry | Grade | Flow Density | Size | Hardness | Application Data | |
| PTA&Laser clad | ||||||
| Iron base alloy Gas atomized |
316, 420, 430,440 | / | / | 80-270mesh 100-270mesh |
/ | By differetn grades, the coating will have medium anti-wear and corrosion perfromance. |
| Nickel base alloy Gas atomized |
Ni15, Ni25 Ni35,Ni45 Ni50,Ni60 Ni65 |
/ | 12-15s/50g 3.5-4g/cm3 | 80-270mesh 100-270mesh |
15-65HRC | By differetn grades, the coating will have different anti-wear and corrosion perfromance. |
| Cobalt base alloy Gas atomized |
Co1#, Co6# Co12# Co21# |
/ | 12-15s/50g 4.3-4.8g/cm3 | 100-270mesh | 28-55HRC | related coating performance, please see our Cobalt base alloy introduction. |
|
Cast/Fused WC |
WC/NiBSi 60/40 65/35 other ratio |
/ | / | 80-270mesh 100-270mesh |
Matrix 35HRC Carbide HV2500 |
For hardfacing of Steel, cast Iron, high-temperature alloy which are subjected to severe abrasion, friction wear, erosion, oxidation etc. |
| Spherical Cast WC blend | SWC/Ni base matrix | / | / | 80-270mesh 100-270mesh |
Matrix 50HRC Carbide 3300HV |
excellent resistance to severe abrasion, corrosion, erosion and oxidation, application for shafts, earth moving equipment, quarry equipement etc. |
| Macro-Crystalline WC blend |
MWC/Ni base Matrix | / | / | 80-270mesh 100-270mesh |
Matrix 50HRC Carbide 2200HV |
Higher thermal stablitity compared with cast tungsten carbide blend. |