You are here:Home > Coating materials > Other special powder
Feedback
| Chemistry | Grade | Flow Density | Size | Hardness | Application Data | |
| Other Special powder | ||||||
| Mo powder Agglomerated and sinter |
Mo:99.5 | SMO | 3.8-4.2 g/cm3 |
90-45um 11-53um |
/ | Piston ring, synchronizing ring, valves, pump and mating parts. Resists fretting and electric arc erosion Good bonding Service up to 320 °C (610°F) |
| NiAl powder clad |
NiAl 95/5 90/10 85/15 |
NiAl | 18-21 s/50g 3.8-4.2 g/cm3 |
90-45um 106-45um |
/ | Self-adhesion bondcoat powder for ceramic and abradable top coatings Exothermic reaction during spraying creates excellent self-bonding coating which is dense and machinable High temperature oxidation and abrasion resistance For salvage and build-up on carbon and corrosion resistant steels Service up to 800°C (1,470 °F) |
| NiCr alloy atomized |
Ni:80 Cr:20 |
Ni20Cr | 17-21 s/50g 4.2-4.5 g/cm3 |
105-45um -53+15um |
/ | Resists high temp. oxidizing and corrosive gases, prevents scalingon carbon and low alloy steels Good bondcoat for ceramic top coats Higher chromium enhances corrosion resistance Sputtering Target powder itself or as bond coat Service up to 980°C (1,800 °F) |
| Ni/graphite | Ni:85 Graphite:15 |
NiC 8515 |
28-35 s/50g 1.8-2.3 g/cm3 |
90-45um | / | coatings are lubricious and suited for friction applications Flame spraying offers good abradablity, Sacrificial coatings good for clearance control, useful up to 900 F(482 C) |
| Pure Tititanium CPTi powder HDH |
Ti:99.5% | Ti995 | 30-40 s/50g 1.4-2.4 g/cm3 |
250-150um 180-75um |
/ | Biocompatibility for medical application; coating with porous structures for implants; corrosion resistant; bond coat for hydroxyapatite. |