You are here:Home > Powder Metallurgy > Diamond tool powder
Feedback
| Chemistry | Grade | Flow Density | Size | Hardness | Application Data | |
| Diamond Tool Powder | ||||||
| Cobalt powder Reduction |
Co:99.9 Ni:0.005 Cu:0.002 Fe:0.005 Pb:0.005 Zn:0.008 Cd:0.001 |
Co999 | 0.4-0.75 g/cm3 |
FSSS: 1.3-1.7um | / | With Co powder added, the holding force and tougness will be improved. |
| Tin powder | Sn:99.5 Fe:0.04 Sb:0.04 As:0.01 Cu:0.02 S:0.001 Pb:0.1 |
Sn995 | / | 75um 53um 45um |
/ | Tin powder will low down the sinter temperature of matrix, and easy to form alloy with other metal. |
| Copper powder | Cu:99.5 Fe:0.02 Sb:0.01 S:0.004 Pb:0.05 |
Cu995 | / | 75um 53um 45um |
/ | Reduce the sinter temperature of matrix. |
| Pre-alloy powder HR533 |
Fe:60-65 Cu:25-35 Sn:3-6 other micro elemnet |
533 | sinter density 8.17g/cm3 |
53um 45um |
HRB90 | sinter temperature:740-760 application: ston, saw blade, cutting. |
| Pre-alloy powder HRHO3 |
Fe:70-75 Cu:19-23 Sn:6-12 Ni:2-4 other micro elemnet |
H03 | sinter density 8.1g/cm3 |
53um 45um |
HRB85 | sinter temperature:730-750 application: Sharpness type, use for hard stone cutting |
| Pre-alloy powder HRHOC |
Fe:70-75 Cu:19-23 Ni:15-20 other micro elemnet |
HOC | sinter density 8.15g/cm3 |
53um 45um |
HRB105 | sinter temperature:840-860 application: As additive of hardness phase and wear resisit phase |
| Pre-alloy powder HRLFO |
Fe:65-70 Cu:19-23 Sn:4-8 Co:7-10 other micro elemnet |
LFO | sinter density 8.0g/cm3 |
53um 45um |
HRB90 | sinter temperature:780-800 application: can improve the hold force, the blade can cut dry. |
| Pre-alloy powder HRHLL |
||||||
| Pre-alloy powder HRHLM |
||||||
| Pre-alloy powder HRLM1 |
||||||
| Pre-alloy powder HRLG |
||||||
| Pre-Alloy powder HRLZ |
||||||