| Chemistry | Grade | Density | Size | Hardness | Application Data | |
| PM/MIM Powder | ||||||
| HR304(L) Stainless Steel Powder Atomized |
Cr:18-20 Ni:8-12 C:0.08(0.03) Si:1max Mn:2max Fe:bal. |
304(L) | app.4.1-4.5 tap.>4.9 g/cm3 |
150um 75um 45um 15um |
34.5HRC | MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.6g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 |
| HR316(L) Stainless steel powder Atomized |
Cr:16-18 Ni:10-14 Mo:2-3 C:0.08(0.03) Si:1max Mn:2max Fe:bal. |
316(L) | app.4.1-4.5 tap.>4.8 g/cm3 |
150um 75um 45um 15um |
36HRC | MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 |
| HR174PH Stainless steel powder Atomized |
Cr:15.5-17.5 Ni:3-5 Nb:0.15-0.45 Cu:3-5 C:0.07 Si:1max Mn:1max Fe:bal. |
17-4PH | app.4.1-4.5 tap.>4.8 g/cm3 |
150um 75um 45um 15um |
35HRC | MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 |
| HR420 Stainless steel powder Atomized |
Cr:12-14 C:0.25max Si:1max Mn:1max Fe:bal. |
420 | app.4.1-4.5 tap.>4.8 g/cm3 |
150um 75um 45um 15um |
HRC50 | MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 |
| HR430 Stainless steel powder Atomized |
Cr:16-18 C:0.12max Si:1max Mn:1max Fe:bal. |
430 | app.4.1-4.5 top.>4.8 g/cm3 |
150um 75um 45um 15um |
HRC51 | MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 |
| HR70Cr | Cr:65-70 C:0.06(0.03) Si:1.0max S:0.03max P:0.03max |
70Cr | / | -75um -45um |
/ | As additive for special part require anti-wear and anti-corrosion, like auto valve shaft guide pipe, seat etc. |
| HR60Mo | Mo:60-65 C:0.04max S:0.15max P:0.06max Si:1.5max |
60Mo | / | 75um 45um 37um 25um |
/ | As additive for special part require anti-wear and anti-corrosion, like auto valve shaft guide pipe, seat etc. |
| HRCr12Mo | Cr:10 Mo:1.5 C:0.06 Mn:0.1 S:0.022 P:0.022 Si：1.0 Fe:bal. |
12CrMo | / | 75micron 53micron 45micron |
/ | this alloy powder contain Cr and Mo content, can provide good anti-wear, anti-corrosion performance, it is usually to produce special part which need above performance. |
| HRMnS | Mn:62-65 S:33-36 O:0.5 Other: 1max |
MnS | / | 300mesh D95:10-12micron |
/ | As additive, function is lubricaiton. |
| HRFeC1# Carbonyl Iron powder |
Fe:98%min C:0.8%max N:0.6%max O:0.4%max |
CF1-1 | App.:2.2min Tap:4.0min |
D10:0.5-1.0um D50:2.0ummax D90:3.0-5.0um |
/ | / |
| HRFeC1# Carbonyl Iron powder |
Fe:98%min C:0.8%max N:0.6%max O:0.4%max |
CF1-2 | App.:2.5min Tap:3.9min |
D10:0.6-1.5um D50:2.0-3.0um D90:4.5-8.0um |
/ | / |
| HRFeC1# Carbonyl Iron powder |
Fe:98%min C:0.8%max N:0.6%max O:0.4%max |
CF1-3 | App.:2.5min Tap:3.8min |
D10:1.0-3.0um D50:3.0-5.0um D90:5.0-12.0um |
/ | / |
| HRFeC1# Carbonyl Iron powder |
Fe:98%min C:0.9%max N:0.7%max O:0.4%max |
CF1-4 | App.:2.2min Tap:3.5min |
D10:1.5-3.5um D50:5.0-6.0um D90:11.5-16.5um |
/ | / |
| HRFeC2# Carbonyl Iron powder |
Fe:99.5%min C:0.05%max N:0.01%max O:0.2%max |
CF2-2 | App.:2.5min Tap:3.8min |
D10:0.9-3.0um D50:3.0-5.0um D90:5.5-12.0um |
/ | / |
| HRFeC2# Carbonyl Iron powder |
Fe:99.5%min C:0.05%max N:0.01%max O:0.2%max |
CF2-3 | App.:2.5min Tap:3.6min |
D10:1.5-3.0um D50:5.0-8.0um D90:10-18um |
/ | / |
| Other Carbonyl Iron powder | we have more than 20grades, please contact our sales to get more details | |||||